Low porosity fireclay brick

Low-porosity fireclay brick is made from low-aluminum mullite as the main raw material, which is formed by high pressure molding and high temperature sintering. The main mineral composition is the mullite phase, and low porosity clay brick has excellent physical properties at high temperatures and resistance to chemical erosion.

Physico-chemical parameters of low-porosity fireclay bricks.

Subject	Index
Al2O3  %	≥45
Fe2O3  %	≤1.3
Bulk density g/cm3	≥2.3
Apparent porosity %	≤16
Cold crush strength MPa	≥65
Creep rate % 1200℃×50h	≤0.05
Thermal shock resistance cycle water cooling at 1100℃	＞10

Features of Low Porosity Clay Brick

1. Low porosity
2. High softening point under load
3. High compressive strength at room temperature
4. Good volumetric stability at high temperatures and good wear resistance.
5. Good anti-penetration and anti-corrosion properties.

Comparison of Low Porosity Clay Bricks and Conventional Clay Bricks

Low porosity clay brick have good stability, no sudden changes in the degree of erosion, service life in 2-3 times longer, than ordinary clay brick, and also in 2 times higher thermal conductivity and specific heat capacity, than ordinary clay brick. Heat capacity per 50% higher, than ordinary clay brick.

Delivery of low-porous clay adobe

Low porosity clay bricks are usually delivered within 7-12 days, excluding special orders.

About Rongsheng Company

Rongsheng has rich manufacturing experience in the refractory industry, especially in the production of refractory bricks and unmolded refractory materials. High alumina brick, high purity corundum bricks, mullite insulation brick, Andalusite bricks and cast bricks are very popular. Rongsheng exports its products to more than 80 countries. Including Russia, South Africa, Bangladesh, Egypt, France, Chile etc. d.

Customers show fireclay bricks

Video about Rongsheng refractory supplier

CContact us